LNP™ ELCRIN™ ML4412B
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRIN ML4412B resin is a 20% glass fiber reinforced Polycarbonate Copolymer, medium flow, impact modified, injection moldable grade with partial component synthesized from Bio source. ELCRIN ML4412B is available in opaque colors only and is an excellent candidate for a broad range of applications that require a combination of stiffness, ductility and good chemical resistance.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性增韧/冲击改性易成型生物基耐化学性中粘度填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 颜色形状 | 粒状不透明色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.33 g/cm³ | ISO 1183 | |
比重 | 1.33 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 10 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 11 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.3 % | Internal | 3.2mm |
横向(Across Flow) | 0.4~0.5 % | Internal | 3.2mm |
吸水率 | 0.1 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.03 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 110 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 100 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 3 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 160 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 165 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 5800 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 5700 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 6300 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 6500 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 17 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 140 J/m | ASTM D256 | |
23℃ (73℉) | 17 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 700 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 25 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 133 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 142 °C | ISO 306/B120 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 26 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 68 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.4 mm | UL94 | Min. |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1.1 GHz | 3.11 - | Internal | |
1.9 GHz | 3.13 - | Internal | |
5 GHz | 3.14 - | Internal | |
10 GHz | 3.16 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 64 E-4 | Internal | |
1.9 GHz | 60 E-4 | Internal | |
5 GHz | 51 E-4 | Internal | |
10 GHz | 63 E-4 | Internal |