LEXAN™ FXE4472L
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN FXE4472L is a 20% glass filled, impact modified polycarbonate with excellent light-shield capability. It is designed for high flow, superior surface appearance, enhance release and good impact ductility.
FXE4472L is available in white color only and ideal for light-shield applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好冲击性增韧/冲击改性光屏蔽良好表面易脱模高流动填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 颜色形状 | 白色 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.33 g/cm³ | ISO 1183 | |
比重 | 1.33 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.3 % | Internal | flow, 3.2 mm |
横向(Across Flow) | 0.4~0.5 % | Internal | xflow, 3.2 mm |
吸水率 | 0.12 % | ISO 62 | 23°C/sat |
吸湿率 | 0.04 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 38 Mpa | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 44 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 3 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 4 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
屈服(yld) | 82 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 5200 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 6050 Mpa | ASTM D638 | 5 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 170 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 920 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 23 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 129 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 134 °C | ASTM D1525 | Rate B/120 |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | -2 % | Internal | 0.4 mm |