LNP™ LUBRICOMP™ DL003EU
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP* DL003EU is a compound based on Polycarbonate resin containing 15% PTFE. Added features of this material include: Easy Molding, UV Stabilized, Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨易脱模抗紫外线 | |||
| 增强填充 | 15% PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.29 g/cm³ | ISO 1183 | |
密度 | 1.28 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.8~0.9 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.8~0.9 % | ASTM D 955 | xflow, 24 hr |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 45 Mpa | ASTM D638 | |
屈服(yld) | 54 Mpa | ISO 527 | |
断裂(brk) | 50 Mpa | ISO 527 | |
断裂(brk) | 50 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 5.6 % | ASTM D638 | |
屈服(yld) | 5.5 % | ISO 527 | |
断裂(brk) | 25.5 % | ASTM D638 | |
断裂(brk) | 9.6 % | ISO 527 | |
弯曲强度 | |||
- | 82 Mpa | ASTM D790 | |
- | 84 Mpa | ISO 178 | |
弯曲模量 | 2300 Mpa | ASTM D790 | |
弯曲模量 | 2300 Mpa | ISO 178 | |
拉伸模量 | 2180 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2200 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.18 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.07 - | ASTM D 3702 | Static COF |
磨损因数 | 60 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 143 J/m | ASTM D256 | |
23℃ (73℉) | 16 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2136 J/m | ASTM D4812 | |
23℃ (73℉) | 100 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 116 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 128 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 73.8 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 74 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 75.5 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 75 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |