LEXAN™ LUX7189
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN LUX7189 is an injection moldable polycarbonate (PC) with an MVR (300°C/1.2kg) 23. It contains non-brominated, non-chlorinated flame retardant systems with UL-94 V0@1.5mm rating. It is designed for high light reflectance and shielding applications with good UV weathering capability.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无氯无溴光反射光屏蔽抗紫外线耐候性 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.3 g/cm³ | ASTM D792 | |
比重 | 1.3 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 22 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | flow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 52 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 110 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 98 Mpa | ISO 178 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2700 Mpa | ISO 178 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2700 Mpa | ISO 527 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 100 J/m | ASTM D256 | |
23℃ (73℉) | 150 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2140 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 59 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ASTM D648 | 3.2mm, unannealed |
维卡软化温度(Vicat) | 140 °C | ASTM D1525 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 65 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
5VB | 2.5 mm | UL94 | |
5VA | 3 mm | UL94 |