LEXAN™ DMX1214
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN DMX1214 is a standard flow Polycarbonate (PC) copolymer resin. Available in both transparent and custom colours, this grade is a good candidate for 5G related devices. Added features of this grade include: Improved Scratch Resistance and Improved Dielectric Performance (lower Df).
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 低介电性红外线穿透耐刮擦易成型共聚物 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.17 g/cm³ | ISO 1183 | |
密度 | 1.17 g/cm³ | ASTM D792 | |
比重 | 1.18 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 16 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 17.1 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.5~0.8 % | Internal | 3.2 mm |
吸水率 | 0.1 % | ASTM D570 | 23°C/24hrs |
吸水率 | 0.3 % | ASTM D570 | 23°C/Saturated |
吸水率 | 0.3 % | ISO 62-1 | |
吸湿率 | 0.14 % | ISO 62 | |
吸湿率 | 0.05 % | ASTM D 570 | 23°C/50% RH/24 hrs |
吸湿率 | 0.14 % | ASTM D 570 | 50% RH, Equilibrium |
比容 | 0.85 cm³/g | ASTM D792 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 77 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 77 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 62 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 64 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 8 % | ISO 527 | 50 mm/min |
断裂(brk) | 92 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 60 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 116 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 101 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2630 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2310 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2830 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2400 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 3 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 133 kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 32 J/m | ASTM D256 | |
-30℃ (-22℉) | 4 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 37 J/m | ASTM D256 | |
23℃ (73℉) | 6 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 93 kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 68 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
铅笔硬度 | |||
1kg | F - | ASTM D 3363 | |
Erichson 划痕深度 | 14 micrometer | Internal | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 133 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 134 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 121 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 121 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 138 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 141 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 142 °C | ISO 306/B120 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 60 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
纵向(Flow) | 60 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 60 E-6/°C | ASTM E831 | -40°C to 95°C, xflow |
横向(Across Flow) | 60 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Min. |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 88 % | ASTM D1003 | 2.54 mm |
雾度 | 0.8 % | ASTM D1003 | 2.54 mm |
折射率 | 1.584 - | ASTM D542 | |
折射率 | 1.584 - | ISO 489 |