LNP™ THERMOCOMP™ DX06413H
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP DX06413H is a compound based on Polycarbonate resin containing 40% Glass Fiber. Added features of this material include: Easy Molding, Mold Release.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 易脱模填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 增强填充 | 40% 玻纤 | |||
技术参数
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
拉伸强度 | |||
断裂(brk) | 84 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 1.1 % | ASTM D638 | |
弯曲强度 | |||
- | 117 Mpa | ASTM D790 | |
弯曲模量 | 11030 Mpa | ASTM D790 | |
拉伸模量 | 10540 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 53 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 373 J/m | ASTM D4812 |