LNP™ ELCRES™ EXL4312
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRES EXL4312 is based on Polycarbonate (PC) siloxane copolymer resin containing 20% glass fiber, medium flow, impact modified, injection moldable grade. EXL4312 has good surface energy and high gloss and is good candidate for a broad range of applications that require a combination of stiffness and ductility.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性良好表面高光泽中粘度共聚物填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 16 g/10min | ASTM D1238 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 90 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 90 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3.5 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 3.2 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
- | 140 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 5400 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 5500 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 5400 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 100 J/m | ASTM D256 | |
23℃ (73℉) | 150 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 780 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1.1 GHz | 3.107 - | Internal | |
1.9 GHz | 3.07 - | Internal | |
5 GHz | 3.103 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 60 E-4 | Internal | |
1.9 GHz | 60 E-4 | Internal | |
5 GHz | 60 E-4 | Internal |