LEXAN™ ML7667
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN ML7667 specialty polycarbonate (PC) resin is a 9% GF reinforced, UV stabilized, flame retarded injection molding grade. This medium flow specialty PC resin combines UL94 V0 @ 1.5mm, 5VB @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR agents with excellent processability, improved release performance and good impact performance. This product is available in limited opaque colors only and may be an excellent candidate for a broad range of applications, i.e. electrical and electronic enclosure applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击阻燃无氯无溴易成型易脱模抗紫外线填充增强 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 颜色形状 | 粒状不透明色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 9% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.26 g/cm³ | ISO 1183 | |
比重 | 1.26 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 8 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 9 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.6 % | Internal | 3.2 mm |
吸水率 | 0.15 % | ISO 62 | 23°C/sat |
吸湿率 | 0.4 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 54 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 46 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 44 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4.4 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 4.4 % | ISO 527 | 5 mm/min |
断裂(brk) | 15 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 13 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
屈服(yld) | 97 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 96 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 3150 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 3400 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 3500 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 3600 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 15 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 25 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 150 J/m | ASTM D256 | |
-30℃ (-22℉) | 10 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 340 J/m | ASTM D256 | |
23℃ (73℉) | 25 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 40 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 146 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 146 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 145 °C | ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 47 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 47 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 70 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 70 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | Pass |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
5VB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 175 V | IEC 60112 |