Lupoy® UF1004CI
PC(聚碳酸酯)
乐金LG化学 (LG Chem)
产品描述
LUPOY PC UF1004CI resin is designed for Light guide panel application. It exhibits an excellent flow-ability, thermal resistance and good Optical properties.
Main Characteristics
-Very low viscosity
-Good optical properties
-Thermal stability
Applications
-Light guide panel
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定良好光学性导光低粘度 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
250°C/1.2 kg | 10 g/10 min | ASTM D1238 | |
300℃/1.2 kg | 70 g/10min | ASTM D1238 | |
收缩率 | |||
- | 0.5~0.7 % | ASTM D 955 | |
吸水率 | 0.15 % | ASTM D570 | 24 hr, 23°C |
吸水率 | 0.32 % | ASTM D570 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ASTM D638 | 23°C, 50 mm/min |
断裂(brk) | 48 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | |
断裂(brk) | 90 % | ASTM D638 | |
弯曲强度 | |||
- | 100 Mpa | ASTM D790 | |
弯曲模量 | 2200 Mpa | ASTM D790 | |
拉伸模量 | 1800 Mpa | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 500 J/m | ASTM D256 | 3.18 mm, 0.25 mm Notch Depth |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 59 J | ASTM D3763 | 3.18 mm, 3.39 m/sec |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 58 M | ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | Annealed, 4.00 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ASTM D648 | Annealed, 4.00 mm |
维卡软化温度(Vicat) | 140 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
线性膨胀系数(CLTE) | |||
- | 68 E-6 mm/mm/℃ | ASTM D 696 | -40 to 82°C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.4 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 91 % | ASTM D1003 | |
雾度 | 0.1~1 % | ASTM D1003 | |
折射率 | 1.583 - | ASTM D542 |