LNP™ ELCRES™ EXL9034
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRES EXL9034 is based on Polycarbonate (PC) siloxane copolymer resin with excellent low temperature ductility, robust flame retardancy (V0/5VA), good processability and electrical tracking resistance. It is UV stabilized with F1 rating and is a good candidate for applications like photovoltaic connectors.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击阻燃易成型短周期成型抗紫外线耐候性共聚物 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.22 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 6 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 7 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | flow, 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | xflow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 55 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 59 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 60 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 70 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 68 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 87 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 84 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2020 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2100 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2090 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2065 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 55 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 66 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 660 J/m | ASTM D256 | |
-30℃ (-22℉) | 52 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 700 J/m | ASTM D256 | |
23℃ (73℉) | 62 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB J/m | ISO 180/1U | 80*10*3 |
-30℃ (-22℉) | NB J/m | ASTM D 4812 | |
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 66 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 147 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 146 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 145 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 115 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 72 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 78 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 78 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 89 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 | Min. |
5VB | 2.5 mm | UL94 | Min. |
5VA | 3 mm | UL94 | Min. |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | |
热线圈起燃性(HWI) | 2 PLC | UL 746A | ≥0.8mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746A | ≥0.8mm |