CALIBRE™ 603-6
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 603-6 Polycarbonate Resin is a branched polycarbonate resin specially designed for multi-wall sheet extrusion. CALIBRE 603-6 offers a high melt strength to calibrate effectively a wide range of multi-wall sheet structures from low to high complexity, such as seven wall sheet. CALIBRE 603-6 offers a wider processing window than CALIBRE 503-5 and is likewise specially designed to give excellent sheet surface quality at high line speeds with a reduced tendency to display chatter marks. CALIBRE 603-6 contains a UV absorber additive, but sheets for outdoor applications require a protective UV-absorbing cap layer. It is recommended to coextrude a 50 micron thick cap layer from CALIBRE 320UV.
Main Characteristics:
Wide processing window
High surface quality
Minimizes chatter marks
Applications:
Low to high complexity multi-wall sheets
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 良好表面抗紫外线高熔体强度 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 挤出片材挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 6 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
吸水率 | 0.15 % | ISO 62 | 24 hr, 23°C |
吸水率 | 0.32 % | ISO 62 | Equilibrium, 23°C, 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ISO 527-2/50 | |
断裂(brk) | 66 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 93 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2400 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2350 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 16 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 55 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 15 kJ/m² | ISO 180/A | |
23℃ (73℉) | 80 kJ/m² | ISO 180/A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 142 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 150 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6 cm/cm/℃ | ISO 11359-2 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 900 °C | IEC 60695-2-12 | |
2mm | 875 °C | IEC 60695-2-12 | |
3mm | 875 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 800 °C | IEC 60695-2-13 | |
2.0mm | 775 °C | IEC 60695-2-13 | |
3.0mm | 775 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
溶液A | 250 V | IEC 60112 | 2.0 mm |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 86~90 % | ASTM D1003 | |
雾度 | 1 % | ASTM D1003 | |
折射率 | 1.586 - | ISO 489 |