LNP™ ELCRES™ CRX9411W
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRES CRX9411W is an amorphous Polycarbonate (PC) copolymer resin that offers medium flow, UL V0 rating @ 1.6 mm for all colors, and high ductility in combination with excellent chemical resistance. This grade is available for custom coloring and may be an excellent candidate for a wide variety of applications that need improved chemical resistance. This grade is subjected to SABIC healthcare management of change policy and formulation lock.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击高韧性阻燃医疗级耐化学性中粘度共聚物 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.2 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 9 cm³/10 min | ISO 1133 | |
300°C/1.2 kg | 9.5 cm³/10 min | ASTM D 1238 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.9 % | Internal | |
横向(Across Flow) | 0.4~0.9 % | Internal | |
吸水率 | 0.3 % | ISO 62-1 | 23°C/24hrs |
吸湿率 | 0.08 % | ISO 62-4 | 23°C/50% RH/24hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 52 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 50 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 100 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 100 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 85 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 80 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2000 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2012 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 1920 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 1858 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 65 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-70℃ (-94℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-70℃ (-94℉) | 570 J/m | ASTM D256 | |
-70℃ (-94℉) | 35 kJ/m² | ISO 180/1A | 80*10*3 |
-60℃ (-76℉) | 609 J/m | ASTM D256 | |
-30℃ (-22℉) | 680 J/m | ASTM D256 | |
23℃ (73℉) | 765 J/m | ASTM D256 | |
23℃ (73℉) | 55 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-70℃ (-94℉) | NB J/m | ASTM D4812 | |
-70℃ (-94℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 61 J | ASTM D3763 | |
仪器化冲击韧性 | |||
23℃ (73℉) | 100 % | ASTM D 3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 146 °C | ASTM D1525 | Rate B/120 |
维卡软化温度(Vicat) | 142 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 142 °C | ISO 306/B50 | Rate B/50 |
维卡软化温度(Vicat) | 144 °C | ISO 306/B120 | Rate B/120 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 70 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 70 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 70 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.6 mm | UL94 | Min. |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+13 Ohm | ASTM D257 | |
介电常数(DK) | |||
100 MHz | 2.82 - | Internal | |
2.47 GHz | 2.78 - | Internal | |
耗散因数(DF) | |||
100 MHz | 66 E-4 | Internal | |
2.47 GHz | 53 E-4 | Internal | |
相比漏电起痕指数(CTI ) | |||
- | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 0 PLC | UL 746A | ≥0.8mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746A | ≥0.8mm |