LNP™ ELCRES™ HR156R
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRES HR156R is a compound based on Copolymer Polycarbonate resin. This resin has higher RTI, better scratch resistance and higher modulus than standard PC. It offers excellent heat resistance performance, good processability and available for opaque or limited transparent colors
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热耐刮擦易脱模高流动 | |||
| 颜色形状 | 粒状透明不透明色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
比重 | 1.2 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
330°C/2.16kg | 42 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
330°C/2.16 kg | 45 g/10 min | ASTM D 1238 | |
收缩率 | |||
纵向(Flow) | 0.6~0.9 % | Internal | 3.2mm |
吸水率 | 0.3 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.23 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 72 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 72 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 62 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6.5 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6.5 % | ISO 527 | 50 mm/min |
断裂(brk) | 90 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 90 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 11 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 102 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2600 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2500 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2620 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2650 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 10 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 20 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 73 J/m | ASTM D256 | |
-30℃ (-22℉) | 10 kJ/m² | ISO 180/1A | 80*10*3 |
-30℃ (-22℉) | 11 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 113 J/m | ASTM D256 | |
23℃ (73℉) | 11 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 12 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 68 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 155 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 155 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 145 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 142 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 160 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 160 °C | ISO 306/B50 | Rate B/50 |
维卡软化温度(Vicat) | 162 °C | ISO 306/B120 | Rate B/120 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 60 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 60 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |