LNP™ STAT-KON™ DD200C
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
PTFE free polycarbonate compounds with ESD safety and good lubricating perfomrance , suitable for Semiconductor and Hard Disk Drive (HDD) and semicon industry. Added features of this material include: Good cleanliness control, low LPC, low ionic, and low outgassing.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电抗静电 ESDEMI/RFI ESD低气味 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
比重 | 1.22 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | Internal | |
横向(Across Flow) | 0.5~0.7 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 53 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 53 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 53 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 46 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.3 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 5.2 % | ISO 527 | 5 mm/min |
断裂(brk) | 10 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 10 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
- | 87 Mpa | ASTM D790 | |
- | 87 Mpa | ISO 178 | |
弯曲模量 | 2200 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2380 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2400 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2340 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 92 kJ/m² | ISO 179/2C | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 115 J/m | ASTM D256 | |
23℃ (73℉) | 10 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1800 J/m | ASTM D4812 | |
23℃ (73℉) | 90 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 138 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ASTM D648 | 3.2 mm, unannealed |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+5~1.0E+9 Ohm | ASTM D257 | |
静电衰减 | 0.1 seconds | FTMS101B | 5000V to <50V |