LNP™ ELCRES™ EXL9334
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRES EXL9334 is based on Polycarbonate (PC) siloxane copolymer resin. It is a UV stabilized, medium flow opaque material suitable for injection molding (IM) and sheet extrusion applications. This grade offers UL94 V0 @ 1.5mm flame retardancy based on non-bromine, non-chlorine FR systems, extreme low temperature ductility (-40°C) characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. It is available in a wide range of opaque colors and is targeted for a wide range of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击阻燃无卤无氯无溴易成型短周期成型抗紫外线耐候性中粘度 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂 | |||
| 颜色形状 | 粒状不透明色 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 9 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | |
横向(Across Flow) | 0.4~0.8 % | Internal | |
吸水率 | 0.4 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.15 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 56 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 115 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 108 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 89 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 87 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2050 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2100 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2100 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2000 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 70 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 685 J/m | ASTM D256 | |
-30℃ (-22℉) | 725 J/m | ASTM D256 | |
23℃ (73℉) | 750 J/m | ASTM D256 | |
23℃ (73℉) | 65 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
-30℃ (-22℉) | NB J/m | ASTM D 4812 | |
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 140 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 118 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 140 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 139 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 141 °C | ISO 306/B120 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 110 °C | UL 746B | |
电气Elec,- | 125 °C | UL 746B | |
强度w/o impact,- | 120 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 61 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 61 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 62 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 65 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | Min. |
5VA | 3 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
1.5mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.5mm | 825 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
相比漏电起痕指数(CTI ) | |||
- | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 3 PLC | UL 746A | 0.75mm |
热线圈起燃性(HWI) | 2 PLC | UL 746A | 3mm |
高电流弧起燃性(HAI) | 1 PLC | UL 746A | 0.75mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746A | 3mm |