LEXAN™ 945
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN 945 Polycarbonate (PC) is an injection moldable non-chlorinated and non-brominated, unfilled flame retardant grade with medium flow. It has an MVR of 10 (300°C/1.2kg) and a UL94 V0@1.0mm, 5VA at 3.0mm rating and is available in various opaque color options.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无氯无溴 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.19 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.6~0.8 % | Internal | flow, 3.2 mm |
吸水率 | 0.15 % | ASTM D570 | 24 hours |
吸水率 | 0.23 % | ASTM D570 | equilibrium, 23C |
吸湿率 | 0.15 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 65 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 125 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 101 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2340 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2270 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 801 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D4812 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 73 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 70 M | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 126 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 143 °C | ASTM D1525 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 120 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
比热容 | 1.25 J/g-°C | ASTM C 351 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 66.6 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 66.6 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
导热系数 | 0.27 W/m-°C | ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | V-2 mm | UL94 | |
V-0 | V-0 mm | UL94 | |
5VA | 5VA mm | UL94 | |
氧指数(LOI) | 35 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | pass |
灼热丝点燃温度(GWIT) | |||
1.0mm | 875 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 2 PLC | UL 746A | |
耐电弧性 | 7 PLC | ASTM D495 | Tungsten |
高电压电弧起痕速率(HVTR) | 4 PLC | UL 746A | |
热线圈起燃性(HWI) | 2 PLC | UL 746A | |
高电流弧起燃性(HAI) | 3 PLC | UL 746A | surface |