LNP™ STAT-KON™ DDF029
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP STAT-KON* DDF029 is a compound based on Polycarbonate resin containing Carbon, Glass Fiber. Added features of this material include: Electrically Conductive. Flame Retardant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃导电填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 增强填充 | 玻纤炭黑玻纤+炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.37 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.44 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.4 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.5 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 0.49 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.2 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.11 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 81 Mpa | ISO 527 | |
断裂(brk) | 81 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 2.9 % | ASTM D638 | |
断裂(brk) | 2.8 % | ISO 527 | |
弯曲强度 | |||
- | 132 Mpa | ASTM D790 | |
- | 134 Mpa | ISO 178 | |
弯曲模量 | 4410 Mpa | ASTM D790 | |
弯曲模量 | 4800 Mpa | ISO 178 | |
拉伸模量 | 4480 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 4600 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 53 J/m | ASTM D256 | |
23℃ (73℉) | 6 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 443 J/m | ASTM D4812 | |
23℃ (73℉) | 32 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 7 J | ASTM D3763 | |
多轴冲击 | 2 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 141 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 135 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 1E+5~1.0E+10 Ohm | ASTM D257 |