LEXAN FST3002 resin is a halogen-free flame retardant PC Copolymer Resin with MVR of 8, suitable for injection molding. This resin is EN45545 R6 HL2 compliant and an ideal candidate for train interior applications (category R6). Available in opaque colors
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.22 g/cm³
| ISO 1183 | |
比重 | 1.22 -
| ASTM D792 | |
熔体体积流动速率(MVR) | | | |
300°C/1.2 kg |
8 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
9 g/10min | ASTM D1238 | |
收缩率 | | | |
纵向(Flow) |
0.5~0.7 % | Internal | |
横向(Across Flow) |
0.5~0.7 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
75 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
74 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
59 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
63 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
6 % | ISO 527 | 50 mm/min |
断裂(brk) |
50 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
50 % | ISO 527 | 50 mm/min |
弯曲强度 | | | |
屈服(yld) |
110 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) |
107 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2600 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2400 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 2450 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 2450 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
7 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) |
7 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) |
9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
9 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
60 J/m | ASTM D256 | |
-30℃ (-22℉) |
6 kJ/m² | ISO 180/1A | 80*10*3 |
-30℃ (-22℉) |
6 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) |
70 J/m | ASTM D256 | |
23℃ (73℉) |
7 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) |
7 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 180/1U | 80*10*3 |
-30℃ (-22℉) |
NB kJ/m² | ISO 180/1U | 80*10*4 |
23℃ (73℉) |
NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) |
NB kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
70 J | ASTM D3763 | |
多轴冲击 | 130 J
| ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
121 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） |
125 °C | ISO 75-2/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
108 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
111 °C | ISO 75-2/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 130 °C
| ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 141 °C
| ISO 306 | Rate A/120 |
维卡软化温度(Vicat) | 130 °C
| ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 130 °C
| ISO 306 | Rate B/50 |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
62 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) |
62 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
NBS 烟密度 | 300 -
| ISO 5696-2 | DS-4, 50 kW/m2, 3mm |
NBS 烟密度 | 600 -
| ISO 5696-2 | VOF4, 50 kW/m2, 3mm |
毒性 | 0.9 -
| ISO 5659-2 | CITG (8 min), 50 kW/m2, 3 mm |
放热率 | 90 kW/m²
| ISO 5660-1 | MAHRE, 50 kW/m2, 3 mm |
欧洲轨道车辆认证 | 2 HL
| EN 45545-2 | |