LNP™ LUBRICOMP™ DX09407H
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP DX09407H is a compound based on High Heat Polycarbonate containing proprietary fillers. Added features of this grade are: Wear Resistant, Healthcare.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨医疗级填充增强 | |||
| 增强填充 | 未指明填充物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.21 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.6~0.8 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.21 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 64 Mpa | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 64 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 56 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 53 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6.8 % | ASTM D638 | Type I, 5 mm/min |
屈服(yld) | 6.9 % | ISO 527 | 5 mm/min |
断裂(brk) | 68 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 111 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 90 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 76.8 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2300 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2080 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2230 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2130 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 139 J/m | ASTM D256 | |
23℃ (73℉) | 11 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 2214 J/m | ASTM D4812 | |
23℃ (73℉) | 191 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 139 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 137 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 7.4E+7 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 7.7E+7 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |