CALIBRE™ 2060-3
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 2060-3 Polycarbonate resin is used in medical applications involving steam or ethylene oxide sterilization - though suitability for use in these applications is dependent upon autoclave cycle times and temperatures. CALIBRE 2060-3 provides exceptional clarity, heat resistance, impact strength and has low contamination levels. The CALIBRE 2000 series of resins have been evaluated with respect to ISO 10993-1 (Biological Evaluation of Medical Devices) and are suitable for use in approved medical applications.
Main Characteristics
Tested under ISO 10993
FDA 21 CFR 177.1580
Lipid resistance
Applications
Medical application
Injection or extrusion applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐热医疗级环氧乙烷灭菌(EtO)耐蒸煮 | |||
| 法规认证 | FDA(食品药品监督管理局)ISO10993(生物相容性) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 3.5 g/10min | ASTM D1238 | |
300℃/1.2 kg | 3.5 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ASTM D 955 | |
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
吸水率 | 0.15 % | ASTM D570 | 24 hr, 23°C |
吸水率 | 0.32 % | ASTM D570 | Equilibrium, 23°C, 50% RH |
吸水率 | 0.15 % | ISO 62 | 24 hr, 23°C |
吸水率 | 0.32 % | ISO 62 | Equilibrium, 23°C, 50% RH |
磨耗 | 45 % | ASTM D 1044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ASTM D638 | 50 mm/min |
屈服(yld) | 60 Mpa | ISO 527-2/50 | |
断裂(brk) | 72.4 Mpa | ASTM D638 | 50 mm/min |
断裂(brk) | 72 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
断裂(brk) | 150 % | ASTM D638 | 50 mm/min |
断裂(brk) | 150 % | ISO 527-2/50 | |
标称断裂伸长率 | 50 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 96.5 Mpa | ASTM D790 | 2.0 mm/min |
- | 96 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2410 Mpa | ASTM D790 | 2.0 mm/min |
弯曲模量 | 2410 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2480 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2480 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 960 J/m | ASTM D256 | |
23℃ (73℉) | 93 kJ/m² | ISO 180/A | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D256 | |
23℃ (73℉) | NB kJ/m² | ISO 180 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 93.8 J | ASTM D3763 | |
拉伸冲击 | 630 kJ/m² | ASTM D 1822 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 74 M | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 146 °C | ASTM D648 | Annealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 146 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 143 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 143 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 132 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 151 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 151 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 68 E-6 cm/cm/℃ | ASTM D 696 | -40 to 82°C |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 % | ASTM D1003 | 3180 µm |
雾度 | 1 % | ASTM D1003 | 3180 µm |
折射率 | 1.586 - | ASTM D542 | |
折射率 | 1.586 - | ISO 489 |