EMERGE™ PC 8702-15 (NA)
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
EMERGE™ PC 8702 Advanced Resin is an ignition-resistant, 20% glass reinforced polycarbonate resin. This resin does not contain chlorine or bromine additives. It is a medium flow PC resin with a mold release system, intended for applications requiring high stiffness. EMERGE PC 8702 has a UL94 V-0 rating at 1.5 mm.
Main Characteristics:
Glass reinforced
Ignition resistant
Applications:
Powered Device Housings
Information technology equipment
Electrical parts
Other structural/internal parts
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高刚性阻燃无氯无溴易脱模填充增强 | |||
| 添加助剂 | 阻燃剂脱模剂 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.33 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 15 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.2~0.4 % | ASTM D 955 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 100 Mpa | ASTM D638 | 3.20 mm,Injection Molded |
拉伸延伸率 | |||
断裂(brk) | 4 % | ASTM D638 | 3.20 mm,Injection Molded |
拉伸模量 | 4000 Mpa | ASTM D638 | 3.20 mm,Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 110 J/m | ASTM D256 | 3.20 mm,Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 145 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 143 °C | ASTM D648 | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 140 °C | ASTM D648 | Unannealed |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | 1.60 mm |
表面电阻率 | 3.0E+14 Ohm | ASTM D257 | 1.80 mm |
介电常数(DK) | |||
1MHz | 3.1 - | ASTM D 150 | 1.60 mm |
相比漏电起痕指数(CTI ) | |||
- | 175 V | IEC 60112 | 3mm |
绝缘强度 | 27 kV/mm | ASTM D149 | 1.60 mm |