LEXAN™ EXL1810T
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN EXL1810T polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade. This resin offers cold temperature (0 °C) ductility in combination with very high flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC resin. LEXAN EXL1810T resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击易成型短周期成型高流动 | |||
| 颜色形状 | 粒状透明不透明色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 33 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 35 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.12 % | ISO 62 | 23°C/sat |
吸湿率 | 0.09 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 59 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 56 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 58 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.8 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5.4 % | ISO 527 | 50 mm/min |
断裂(brk) | 118.9 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 118.6 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 99 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 92 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2350 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2250 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2360 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2400 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 40 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 65 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 220 J/m | ASTM D256 | |
-30℃ (-22℉) | 30 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 702 J/m | ASTM D256 | |
23℃ (73℉) | 650 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 79 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度L | 90 L | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 117 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 138 °C | ASTM D1525 | Rate A/50 |
维卡软化温度(Vicat) | 140 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 137 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 120 °C | UL 746B | |
电气Elec,- | 130 °C | UL 746B | |
强度w/o impact,- | 130 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
纵向(Flow) | 65 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 74 E-6/°C | ASTM E831 | -40°C to 95°C, xflow |
横向(Across Flow) | 74 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | Min. |
V-2 | 1.5 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 825 °C | IEC 60695-2-12 | |
1.5mm | 825 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.8mm | 825 °C | IEC 60695-2-13 | |
1.5mm | 825 °C | IEC 60695-2-13 | |
3.0mm | 850 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+15 Ohm | ASTM D257 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 82 % | ASTM D1003 | 2.54 mm |
雾度 | 3 % | ASTM D1003 | 2.54 mm |