LEXAN™ BX7241
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN BX7241 Polycarbonate (PC) is an injection moldable non-chlorinated/brominated, unfilled flame retardant grade that has good impact and processability. It has an MVR of 18 (300°C/1.2kg), UL94 V0@0.6mm, 5VA at 3.0mm rating and can be ideal for thin wall applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击阻燃无氯无溴易成型 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.2 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
260°C/2.16 kg | 18 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
260°C/2.16 kg | 18 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.6 % | Internal | flow, 3.2 mm |
吸水率 | 0.2 % | ISO 62 | 23°C/sat |
吸湿率 | 0.1 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 67 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 62 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 45 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 65 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4.4 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 4.2 % | ISO 527 | 50 mm/min |
断裂(brk) | 100 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 90 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 107 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 99 Mpa | ISO 178 | 2 mm/min |
断裂(brk) | 105 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 98 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2450 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2600 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2500 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2500 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 11 kJ/m² | ISO 179/1eA | 80*10*4mm, Cut |
0℃ (32℉) | 12 kJ/m² | ISO 179/1eA | 80*10*4mm, Cut |
23℃ (73℉) | 37 kJ/m² | ISO 179/1eA | 80*10*4mm, Cut |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 190 J/m | ASTM D256 | |
-30℃ (-22℉) | 11 kJ/m² | ISO 180/1A | 80*10*4 |
0℃ (32℉) | 420 J/m | ASTM D256 | |
0℃ (32℉) | 11 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 690 J/m | ASTM D256 | |
23℃ (73℉) | 28 kJ/m² | ISO 180/1A | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 60 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 103 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 93 °C | ASTM D648 | 3.2mm, unannealed |
维卡软化温度(Vicat) | 111 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 112 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 109 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 59 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 59 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 59 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 59 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 75 °C | IEC 60695-10-2 | Pass |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.2 mm | UL94 | |
V-1 | 0.5 mm | UL94 | |
V-0 | 0.6 mm | UL94 | |
5VB | 1.5 mm | UL94 | |
5VA | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 960 °C | IEC 60695-2-12 | pass |
灼热丝点燃温度(GWIT) | |||
1.0mm | 800 °C | IEC 60695-2-13 | |
1.5mm | 825 °C | IEC 60695-2-13 | |
3.0mm | 825 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
表面电阻率 | 2.0E+15 Ohm | ASTM D257 | |
相比漏电起痕指数(CTI ) | |||
- | 3 PLC | UL 746A | |
热线圈起燃性(HWI) | 4 PLC | UL 746A |