LNP™ ELCRIN™ EXL9414PB
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRIN EXL9414PB polycarbonate (PC) siloxane copolymer resin is a medium flow, non-chlorinated, non-brominated flame retardant opaque injection molding (IM) grade with major component synthesized from Bio source. This resin offers low temperature ductility (-30°C), thin wall flame retardant capability (UL94 V0 @0.8mm), and in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard PC. ELCRIN EXL9414PB copolymer resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications, especially the housing of fast-charging mobile phones.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击阻燃无氯无溴易成型短周期成型易脱模生物基中粘度 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 12 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 13.5 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 55 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 56 Mpa | ISO 527 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.3 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 4.9 % | ISO 527 | 50 mm/min |
断裂(brk) | 89 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 63 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 90 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 86 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2200 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2184 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2117 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2109 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 48 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 81 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 670 J/m | ASTM D256 | |
-30℃ (-22℉) | 51 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 962 J/m | ASTM D256 | |
23℃ (73℉) | 77 kJ/m² | ISO 180/1A | 80*10*3 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 123 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 124 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 110 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 111 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 137 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 138 °C | ISO 306/B120 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 77.1 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 91.1 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 83.4 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 95.4 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 | Min. |
灼热丝点燃温度(GWIT) | |||
1.0mm | 825 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1.1 GHz | 2.87 - | Internal | |
1.9 GHz | 2.82 - | Internal | |
5 GHz | 2.82 - | Internal | |
10 GHz | 2.83 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 60 E-4 | Internal | |
1.9 GHz | 60 E-4 | Internal | |
5 GHz | 60 E-4 | Internal | |
10 GHz | 60 E-4 | Internal |