LNP™ ELCRIN™ EXL8332TCC
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRIN EXL8332TCC is based on Polycarbonate (PC) siloxane copolymer resin. Added features of this grade include: 25% Post Consumer Recycle (PCR) content, Excellent Low Temperature (-20~-30 °C) ductility in combination with Medium Flow characteristics and Excellent Processability with opportunities for shorter IM cycle times compared to standard PC. This is a general purpose product available in Transparent and Opaque colors and is an excellent candidate for a broad range of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击红外线穿透易成型短周期成型高流动中粘度含回收料 | |||
| 颜色形状 | 粒状透明半透明不透明色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 11 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 12 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2mm |
吸水率 | 0.17 % | ISO 62-1 | 23°C/saturated |
吸湿率 | 0.11 % | ISO 62 | 23°C/50%RH |
回收料含量(PCR) | 25 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 57 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 63 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 63 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 110 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 115 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 90 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 88 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2140 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2070 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2140 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 2150 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 34 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 66 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 610 J/m | ASTM D256 | |
-30℃ (-22℉) | 46 kJ/m² | ISO 180/1A | 80*10*3 |
-20℃ (-4℉) | 690 J/m | ASTM D256 | |
23℃ (73℉) | 800 J/m | ASTM D256 | |
23℃ (73℉) | 61 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
-30℃ (-22℉)总能量 | 85 J | ASTM D3763 | |
23℃ (73℉)总能量 | 71 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 119 °C | ASTM D648 | 3.2mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 119 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 147 °C | ASTM D1525 | Rate A/50 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 67 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 69 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.4 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
3.0mm | 875 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+15 Ohm | ASTM D257 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 86 % | ASTM D1003 | 2.54mm |
雾度 | 2.2 % | ASTM D1003 | 2.54mm |