LNP™ THERMOCOMP™ DX11354
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
This is a PC compound with good plating, surface and mechanical performance, a good candidate for Laser Direct Structuring applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好表面电镀/真空镀激光直接成型(LDS) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.27 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 12 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.6~0.65 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.6~0.65 % | ASTM D 955 | xflow, 24 hr |
吸湿率 | 0.01 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 52 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.7 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 64 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 91 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 90 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2300 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2560 Mpa | ASTM D638 | 50 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 750 J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 63 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 69 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1 GHz | 2.92 - | IEC 60250 | |
耗散因数(DF) | |||
1 GHz | 70 E-4 | IEC 60250 |