LNP™ ELCRIN™ EXL8452TCC
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRIN EXL8452TCC polycarbonate (PC) siloxane copolymer resin is a transparent injection molding grade with 50% post consumer recycle (PCR) content. This resin offers excellent low temperature (-20~-30 °C) ductility in combination with medium flow characteristics and excellent processability with opportunities for shorter IM cycle times compared to standard PC. ELCRIN EXL8452TCC resin is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击红外线穿透易成型短周期成型中粘度含回收料 | |||
| 颜色形状 | 粒状透明半透明不透明色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.2 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 11 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 12 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2mm |
回收料含量(PCR) | 50 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 59 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 61 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 65 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5.9 % | ISO 527 | 50 mm/min |
断裂(brk) | 110 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 110 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 95 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 89 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2290 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2240 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2200 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2240 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 26 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 79 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 200 J/m | ASTM D256 | |
-30℃ (-22℉) | 320 J/m | ASTM D256 | |
-30℃ (-22℉) | 24 kJ/m² | ISO 180/1A | 80*10*3 |
-20℃ (-4℉) | 600 J/m | ASTM D256 | |
0℃ (32℉) | 870 J/m | ASTM D256 | |
23℃ (73℉) | 950 J/m | ASTM D256 | |
23℃ (73℉) | 73 kJ/m² | ISO 180/1A | 80*10*3 |
仪器化落镖冲击能量 | |||
-30℃ (-22℉)总能量 | 82 J | ASTM D3763 | |
23℃ (73℉)总能量 | 77 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度L | 88 L | ASTM D 785 | |
洛氏硬度R | 120 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 136 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 141 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 142 °C | ISO 306/B120 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 73 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 77 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 74 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 83 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.4 mm | UL94 | Min. |
氧指数(LOI) | 36 % | ISO 4589 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 875 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+16 Ohm | ASTM D257 | |
介电常数(DK) | |||
1.1 GHz | 2.86 - | Internal | |
1.9 GHz | 2.79 - | Internal | |
5 GHz | 2.8 - | Internal | |
10 GHz | 2.84 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 61 E-4 | Internal | |
1.9 GHz | 56 E-4 | Internal | |
5 GHz | 51 E-4 | Internal | |
10 GHz | 54 E-4 | Internal | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 86 % | ASTM D1003 | 2.54mm |
雾度 | 2 % | ASTM D1003 | 2.54mm |