EMERGE™ PC 8330-10
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
EMERGE™ PC 8330-10 advanced resin is a transparent, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. This resin combines good mechanical and high heat properties, maintains excellent processability and contains mold release agent. EMERGE™ PC 8330-10 has a UL94 V0 rating at 2.5 mm.
Applications:
A broad range of injection molded applications in the lighting, electronics, electrical and information technology equipment markets.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热阻燃无氯无溴无红磷易成型易脱模 | |||
| 添加助剂 | 阻燃剂脱模剂 | |||
| 颜色形状 | 粒状透明 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/50 | 3.20 mm,Injection Molded |
断裂(brk) | 58 Mpa | ISO 527-2/50 | 3.20 mm,Injection Molded |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | 3.20 mm,Injection Molded |
断裂(brk) | 100 % | ISO 527-2/50 | 3.20 mm,Injection Molded |
拉伸模量 | 2400 Mpa | ISO 527-2/50 | 3.20 mm,Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
- | 750 J/m | ISO 180 | 3.20 mm,Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 151 °C | ISO 306 | A120 |
维卡软化温度(Vicat) | 143 °C | ISO 306/B50 | |
球压痕温度 | 123 °C | IEC 598-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 2.5 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
2mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 850 °C | IEC 60695-2-13 | |
2.0mm | 850 °C | IEC 60695-2-13 | |
3.0mm | 850 °C | IEC 60695-2-13 | |
针焰试验 | 1.5 mm | IEC 60695-2-2 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 85~89 % | ASTM D1003 |