LUPOY PC 1600-03 resin is designed for extrusion products. It exhibits an excellent physical property balance of
heat resistance, transparency and impact strength.
Main Characteristics
• High viscosity
• High melt strength
Applic
基本信息
| 原厂资料 | 物性表-ASTM(英文) |
| 产品特性 | 高粘度高熔体强度 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1200 kg/m³
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
3 g/10min | ASTM D1238 | |
收缩率 | | | |
- |
0.005~0.007 mm/mm | ASTM D 955 | |
吸水率 | 0.15 %
| ASTM D570 | 24 hrs, 23℃ |
吸水率 | 0.32 %
| ASTM D570 | equilibrium, 50%RH, 23℃ |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
60 Mpa | ASTM D638 | 23℃,50 mm/min |
断裂(brk) |
72 Mpa | ASTM D638 | |
拉伸延伸率 | | | |
屈服(yld) |
6 % | ASTM D638 | |
断裂(brk) |
150 % | ASTM D638 | |
弯曲强度 | | | |
- |
96 Mpa | ASTM D790 | |
弯曲模量 | 2410 Mpa
| ASTM D790 | |
拉伸模量 | 2410 Mpa
| ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
950 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
NB J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
146 °C | ASTM D648 | 4 mm,annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
132 °C | ASTM D648 | 4 mm,Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
143 °C | ASTM D648 | 4 mm,annealed |
维卡软化温度(Vicat) | 151 °C
| ASTM D1525 | 50℃ /hr, 50N Load |
线性膨胀系数(CLTE) | | | |
- |
68 E-6 mm/mm/℃ | ASTM D 696 | -40 to 82℃ |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 %
| ASTM D1003 | |
雾度 | 0.7~1.5 %
| ASTM D1003 | |
折射率 | 1.586 -
| ASTM D542 | |