LNP™ ELCRES™ CRX1414U
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP ELCRES CRX1414U is an UV stabilized, amorphous Polycarbonate (PC) copolymer resin that offers medium flow, high ductility in combination with excellent chemical resistance. This grade is available for custom coloring and may be an excellent candidate for a wide variety of applications that need improved chemical resistance.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击高韧性抗紫外线耐化学性中粘度共聚物 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.2 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 9 cm³/10 min | ISO 1133 | |
300°C/1.2 kg | 9.5 cm³/10 min | ASTM D 1238 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.9 % | Internal | |
横向(Across Flow) | 0.4~0.9 % | Internal | |
吸水率 | 0.3 % | ISO 62-1 | 23°C/24hrs |
吸湿率 | 0.08 % | ISO 62-4 | 23°C/50% RH/24hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 52 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 50 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 59 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 100 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 100 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 88 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 83 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2050 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2062 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 1900 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 1850 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 65 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
简支梁无缺口(Charpy Unnotched) | |||
-70℃ (-94℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-70℃ (-94℉) | 670 J/m | ASTM D256 | |
-70℃ (-94℉) | 35 kJ/m² | ISO 180/1A | 80*10*3 |
-60℃ (-76℉) | 718 J/m | ASTM D256 | |
-30℃ (-22℉) | 727 J/m | ASTM D256 | |
23℃ (73℉) | 813 J/m | ASTM D256 | |
23℃ (73℉) | 55 kJ/m² | ISO 180/1A | 80*10*3 |
悬臂梁无缺口(Izod Unnotched) | |||
-70℃ (-94℉) | NB J/m | ASTM D4812 | |
-70℃ (-94℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
23℃ (73℉) | NB J/m | ASTM D4812 | |
23℃ (73℉) | NB kJ/m² | ISO 180/1U | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 63 J | ASTM D3763 | |
仪器化冲击韧性 | |||
23℃ (73℉) | 100 % | ASTM D 3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 137 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 136 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 143 °C | ASTM D1525 | Rate B/120 |
维卡软化温度(Vicat) | 141 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 141 °C | ISO 306/B50 | Rate B/50 |
维卡软化温度(Vicat) | 142 °C | ISO 306/B120 | Rate B/120 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 70 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 70 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 70 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Min. |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+13 Ohm | ASTM D257 | |
介电常数(DK) | |||
100 MHz | 2.82 - | Internal | |
2.47 GHz | 2.78 - | Internal | |
耗散因数(DF) | |||
100 MHz | 66 E-4 | Internal | |
2.47 GHz | 53 E-4 | Internal |