CALIBRE™ 301-10
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 300-10 Polycarbonate resins offer exceptional impact resistance, heat distortion resistance, and optical clarity. The CALIBRE 300-10 series products are available in 4 additive packages: CALIBRE 300: No mold release or UV Stabilizer. CALIBRE 301: Mold release. CALIBRE 302: UV stabilizer. CALIBRE 303: Mold release and UV stabilizer
Govt. and Industry Standards:
CSA (Canadian Standards Association)
Underwriters Laboratory, Inc. (UL)
Applications:
Appliances
Storage media housings
Business equipment
Electrical components
Lighting
Transportation
Houseware
Recreation
Packaging applications
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高冲击耐热易脱模 | |||
| 添加助剂 | 脱模剂 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
吸水率 | 0.15 % | ISO 62 | 24 hr, 23°C |
吸水率 | 0.32 % | ISO 62 | Equilibrium, 23°C, 50% RH |
磨耗 | 45 % | ISO 9352 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/50 | |
断裂(brk) | 71 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 150 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 97 Mpa | ISO 178 | 2.0 mm/min |
弯曲模量 | 2400 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 2300 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 13 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 35 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 90 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 73 M | ISO 2039-2 | |
洛氏硬度R | 118 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 144 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 141 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 125 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 149 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6 cm/cm/℃ | ISO 11359-2 | |
球压痕温度 | 125 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 3 mm | UL94 | |
V-2 | 0.75 mm | UL94 | |
V-2 | 1.5 mm | UL94 | |
氧指数(LOI) | 26 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 900 °C | IEC 60695-2-12 | |
2mm | 875 °C | IEC 60695-2-12 | |
3mm | 875 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 800 °C | IEC 60695-2-13 | |
2.0mm | 775 °C | IEC 60695-2-13 | |
3.0mm | 775 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
介电常数(DK) | |||
60 Hz | 3 - | IEC 60250 | |
100Hz | 3 - | IEC 60250 | |
1MHz | 3 - | IEC 60250 | |
耗散因数(DF) | |||
50 Hz | 10 E-4 | IEC 60250 | |
1MHz | 20 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
溶液A | 250 V | IEC 60112 | 2.0 mm |
绝缘强度 | 17 kV/mm | IEC 60243-1 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 89 % | ASTM D1003 | |
雾度 | 1 % | ASTM D1003 | |
折射率 | 1.586 - | ISO 489 |