EMERGE™ PC 8070-15
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
EMERGE™ PC 8070-15 advanced resin is an opaque, ignition resistant PC resin that contains no chlorinated or brominated or phosphorous based additives. This resin contains mould release and it is UV stabilized. It combines good mechanical and high heat properties and maintains excellent processability. EMERGE™ PC 8070-15 has a UL 94 V-0 rating at 0.7 mm. and is F1 rated according to UL746C
Applications:
Electrical
Electronics
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐热阻燃无氯无溴无红磷易脱模抗紫外线 | |||
| 添加助剂 | 阻燃剂紫外线稳定剂脱模剂 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 15 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.5~0.7 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/50 | |
断裂(brk) | 70 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2/50 | |
断裂(brk) | 110 % | ISO 527-2/50 | |
弯曲强度 | |||
- | 95 Mpa | ISO 178 | |
弯曲模量 | 2350 Mpa | ISO 178 | |
拉伸模量 | 2400 Mpa | ISO 527-2/50 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 25 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 65 kJ/m² | ISO 180/A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 143 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 140 °C | ISO 75-2/A | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 124 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 148 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 70 E-6 cm/cm/℃ | ISO 11359-2 | |
球压痕温度 | 125 °C | IEC 60335-1 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.7 mm | UL94 | |
5VB | 2 mm | UL94 | |
5VA | 2.5 mm | UL94 | |
氧指数(LOI) | 35 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
2mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 800 °C | IEC 60695-2-13 | |
2.0mm | 800 °C | IEC 60695-2-13 | |
3.0mm | 800 °C | IEC 60695-2-13 | |
紫外线暴露,水暴露试验和浸渍 | F1 - | UL 746C | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
介电常数(DK) | |||
1 Hz | 2.7 - | IEC 60250 | |
50 Hz | 2.7 - | IEC 60250 | |
耗散因数(DF) | |||
1 Hz | 10 E-4 | IEC 60250 | |
50 Hz | 10 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
溶液A | 225 V | IEC 60112 | |
绝缘强度 | 17 kV/mm | IEC 60243-1 |