LEXAN™ EX1332T - Americas
LEXAN™ EX1332T - Americas
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN EX1332T polycarbonate resin is designed for use in multi-wall sheet or profile extrusion applications. It contains branched polycarbonate resin, release, and is UV stabilized. It is available in a limited number of colors.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 抗紫外线 |
| 添加助剂 | 紫外线稳定剂脱模剂 |
| 成型方式 | 挤出片材挤出型材挤出 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.2 g/cm³
| ISO 1183 | |
比重 | 1.2 -
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
3 g/10min | ASTM D1238 | |
收缩率 | | | |
纵向(Flow) |
0.5~0.7 % | Internal | flow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
61 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
58 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
6.2 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
96.3 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | | | |
屈服(yld) |
97 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2330 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2200 Mpa
| ASTM D638 | 5 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
156 J/m | ASTM D256 | |
23℃ (73℉) |
812 J/m | ASTM D256 | |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
72 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
141 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
131 °C | ASTM D648 | 3.2 mm, unannealed |
维卡软化温度(Vicat) | 146 °C
| ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 148 °C
| ISO 306 | Rate B/120 |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
65 E-6/°C | ASTM E831 | -40°C to 40°C |
横向(Across Flow) |
68 E-6/°C | ASTM E831 | -40°C to 40°C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
0.8 mm | UL94 | |