LNP™ LUBRILOY™ D2000I
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP LUBRILOY D2000I is a compound based on Polycarbonate resin containing Proprietary Lubricant. Added features of this material include: Wear Resistant, High Impact.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐磨 | |||
| 添加助剂 | 润滑剂 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.17 g/cm³ | ASTM D792 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 49 Mpa | ASTM D638 | |
断裂(brk) | 54 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 5.6 % | ASTM D638 | |
断裂(brk) | 130 % | ASTM D638 | |
弯曲强度 | |||
- | 68 Mpa | ASTM D790 | |
弯曲模量 | 1860 Mpa | ASTM D790 | |
摩擦系数 | 0.32 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.22 - | ASTM D 3702 | Static COF |
磨损因数 | 35 E-10 in5·min/ft·lb·hr | ASTM D 3702 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 43 kJ/m² | ISO 180/1A | 80*10*4 |
-40℃ (-40℉) | 542 J/m | ASTM D256 | |
23℃ (73℉) | 779 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1762 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 120 °C | ASTM D648 | 3.2 mm, unannealed |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 131 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 80.1 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 135 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 85.4 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |