LNP™ ELCRES™ EXL1212L
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRES EXL1212L polycarbonate (PC) siloxane copolymer resin is a medium to high flow opaque injection molding (IM) grade. This resin offers good low temperature -20°C ductility and weld line appearance in combination with excellent processability with opportunities for shorter IM cycle times compared to standard PC. ELCRES EXL1212L resin is a product available in wide range of opaque colors and specifically designed for chemical plating process.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击易成型短周期成型电镀/真空镀高流动共聚物 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.18 g/cm³ | ISO 1183 | |
比重 | 1.18 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 14 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 15 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 53 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 53 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 54 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 55 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 6 % | ISO 527 | 50 mm/min |
断裂(brk) | 90 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 90 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 84 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 82 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2090 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2050 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2040 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2080 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 38 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 50 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 320 J/m | ASTM D256 | |
-30℃ (-22℉) | 430 J/m | ASTM D256 | |
-30℃ (-22℉) | 38 kJ/m² | ISO 180/1A | 80*10*3 |
-20℃ (-4℉) | 450 J/m | ASTM D256 | |
0℃ (32℉) | 520 J/m | ASTM D256 | |
23℃ (73℉) | 580 J/m | ASTM D256 | |
23℃ (73℉) | 49 kJ/m² | ISO 180/1A | 80*10*3 |
仪器化落镖冲击能量 | |||
-30℃ (-22℉)总能量 | 63 J | ASTM D3763 | |
23℃ (73℉)总能量 | 62 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度L | 82 L | ASTM D 785 | |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 135 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 122 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 121 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 140 °C | ISO 306/B50 | Rate B/50 |
维卡软化温度(Vicat) | 140 °C | ISO 306/B120 | Rate B/120 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 65 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 74 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 66 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 80 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.4 mm | UL94 | Min. |
氧指数(LOI) | 29 % | ISO 4589 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 850 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+16 Ohm | ASTM D257 | |
介电常数(DK) | |||
1.1 GHz | 2.83 - | Internal | |
1.9 GHz | 2.9 - | Internal | |
5 GHz | 2.77 - | Internal | |
10 GHz | 2.83 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 60 E-4 | Internal | |
1.9 GHz | 58 E-4 | Internal | |
5 GHz | 46 E-4 | Internal | |
10 GHz | 49 E-4 | Internal |