LEXAN™ HF3510R resin is a 39 MFR polycarbonate, MVR of 34. Mold release. Easy processing. Suitable for automotive applications, including bezels. Available only in opaque colors.
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.2 g/cm³
| ISO 1183 | |
比重 | 1.2 -
| ASTM D792 | |
熔体体积流动速率(MVR) | | | |
300°C/1.2 kg |
34 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
36 g/10min | ASTM D1238 | |
收缩率 | | | |
纵向(Flow) |
0.5~0.7 % | Internal | 3.2 mm |
纵向(Flow) |
0.5~0.7 % | Internal | on Tensile Bar |
横向(Across Flow) |
0.5~0.7 % | Internal | 3.2 mm |
吸水率 | 0.3 %
| ISO 62-1 | 23°C/saturated |
吸湿率 | 0.1 %
| ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
62 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
60 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
55 Mpa | ISO 527 | 50 mm/min |
断裂(brk) |
58 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
6 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) |
6 % | ISO 527 | 50 mm/min |
断裂(brk) |
110 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
100 % | ISO 527 | 50 mm/min |
弯曲强度 | | | |
屈服(yld) |
100 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) |
85 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2400 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2300 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 2400 Mpa
| ASTM D638 | 50 mm/min |
拉伸模量 | 2300 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
11 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) |
5 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) |
55 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
12 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
23℃ (73℉) |
NB kJ/m² | ISO 179/1eU | Unnotch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | | | |
-30℃ (-22℉) |
55 J/m | ASTM D256 | |
-30℃ (-22℉) |
11 kJ/m² | ISO 180/1A | 80*10*3 |
-30℃ (-22℉) |
4 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) |
690 J/m | ASTM D256 | |
23℃ (73℉) |
55 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) |
12 kJ/m² | ISO 180/1A | 80*10*4 |
仪器化落镖冲击能量 | | | |
23℃ (73℉)总能量 |
66 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
135 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） |
130 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
0.45 Mpa (66 psi)（4.6kg/cm²） |
133 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
124 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
122 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） |
121 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 139 °C
| ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 139 °C
| ISO 306/B50 | |
维卡软化温度(Vicat) | 140 °C
| ISO 306/B120 | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
72 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) |
70 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) |
78 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) |
78 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
导热系数 | 0.2 W/m-°C
| ISO 8302 | |
球压痕温度 | 125 °C
| IEC 60695-10-2 | PASS |