CALIBRE™ 603-2
PC(聚碳酸酯)
盛禧奥(TRINSEO)
产品描述
CALIBRE™ 603-2 Resin is specially designed for extrusion of super heavy wall sheet and very complex profiles. This resin offers exceptional high melt strength for effective calibration of complex structures, and excellent surface quality. The resin is UV bulk stabilized, but for outdoor use, co-extrusion with a UV cap is needed. It is recommended to apply a 50 micron layer of CALIBRE™ 320UV.
Applications
Multi wall sheet extrusion and profile extrusion
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好表面抗紫外线高熔体强度 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 挤出片材挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
密度 | 1.2 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 1.8 g/10min | ASTM D1238 | |
300℃/1.2 kg | 1.8 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 63 Mpa | ASTM D638 | 4.00 mm, Injection Molded |
屈服(yld) | 63 Mpa | ISO 527-2/50 | 4.00 mm, Injection Molded |
断裂(brk) | 51 Mpa | ASTM D638 | 4.00 mm, Injection Molded |
断裂(brk) | 51 Mpa | ISO 527-2/50 | 4.00 mm, Injection Molded |
拉伸延伸率 | |||
屈服(yld) | 6.3 % | ASTM D638 | 4.00 mm, Injection Molded |
屈服(yld) | 6.3 % | ISO 527-2/50 | 4.00 mm, Injection Molded |
断裂(brk) | 50 % | ASTM D638 | 4.00 mm, Injection Molded |
断裂(brk) | 50 % | ISO 527-2/50 | 4.00 mm, Injection Molded |
弯曲强度 | |||
- | 93.1 Mpa | ASTM D790 | 4.00 mm, Injection Molded |
- | 93.1 Mpa | ISO 178 | 4.00 mm, Injection Molded |
弯曲模量 | 2400 Mpa | ASTM D790 | 4.00 mm, Injection Molded |
弯曲模量 | 2400 Mpa | ISO 178 | 4.00 mm, Injection Molded |
拉伸模量 | 2350 Mpa | ASTM D638 | 4.00 mm, Injection Molded |
拉伸模量 | 2400 Mpa | ISO 527-2/50 | 4.00 mm, Injection Molded |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 69 kJ/m² | ISO 179/1eA | Injection Molded |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 800 J/m | ASTM D256 | 4.00 mm, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 140 °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 140 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 127 °C | ASTM D648 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 127 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 146 °C | ASTM D1525 | Rate A (50°C/h), Loading 2 (50 N) |
维卡软化温度(Vicat) | 146 °C | ISO 306/B50 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 |