LEXAN™ EXL8454
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN EXL8454 is a PC/siloxane copolymer resin with medium flow, excellent low temperature impact and 50% post consumer recycle content. Limited availability and restricted color only. Higher color variability and contamination risks including black specs needs to be considered before approval for use in applications
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击含回收料 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.2 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 10 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.15 % | - | 23°C/24hrs |
回收料含量(PCR) | 50 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 57 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 55 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 100 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 90 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2100 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 2200 Mpa | ASTM D638 | 5 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-40℃ (-40℉) | 54 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) | 58 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
-30℃ (-22℉) | 27 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
23℃ (73℉) | 67 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 65 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-40℃ (-40℉) | 650 J/m | ASTM D256 | |
-30℃ (-22℉) | 700 J/m | ASTM D256 | |
23℃ (73℉) | 800 J/m | ASTM D256 | |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 70 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 123 °C | ASTM D648 | 3.2mm, unannealed |
维卡软化温度(Vicat) | 145 °C | ASTM D1525 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 60 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 825 °C | IEC 60695-2-12 | |
1.5mm | 850 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.75mm | 850 °C | IEC 60695-2-13 | |
1.0mm | 850 °C | IEC 60695-2-13 | |
1.0mm | 875 °C | IEC 60695-2-13 | |
1.5mm | 875 °C | IEC 60695-2-13 | |
3.0mm | 875 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+15 Ohm | ASTM D257 | |
介电常数(DK) | |||
1MHz | 3 - | ASTM D 150 | |
耗散因数(DF) | |||
1MHz | 93 E-4 | ASTM D150 | |
绝缘强度 | 15 kV/mm | ASTM D149 | in oil, 0.8 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746A | ≥3 mm |