LNP™ COLORCOMP™ 121C
LNP™ COLORCOMP™ 121C
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP* COLORCOMP* 121C is an unfilled compound based on Polycarbonate resin. Added features of this grade include: Non-Halogenated, UL Rated HB. Good for small, intricate parts.
基本信息
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.19 g/cm³
| ASTM D792 | |
比重 | 1.2 -
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
17.5 g/10min | ASTM D1238 | |
收缩率 | | | |
纵向(Flow) |
0.5~0.7 % | Internal | flow, 3.2 mm |
吸水率 | 0.15 %
| ASTM D570 | 24 hours |
吸水率 | 0.58 %
| ASTM D570 | equilibrium, 100°C |
吸水率 | 0.35 %
| ASTM D570 | equilibrium, 23C |
比容 | 0.83 cm³/g
| ASTM D792 | |
磨耗 | 10 mg/1000cy
| ASTM D 1044 | CS-17, 1 kg |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
62 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
68 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | | | |
屈服(yld) |
7 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) |
125 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | | | |
屈服(yld) |
96 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2340 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
694 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
3204 J/m | ASTM D4812 | |
仪器化落镖冲击能量 | | | |
23℃ (73℉)峰值 |
62 J | ASTM D3763 | |
落锤冲击 | 169 J
| ASTM D 3029 | |
拉伸冲击 | 546 kJ/m²
| ASTM D 1822 | Type S |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 70 M
| ASTM D 785 | |
洛氏硬度R | 118 R
| ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
137 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
129 °C | ASTM D648 | 6.4 mm, unannealed |
维卡软化温度(Vicat) | 154 °C
| ASTM D1525 | Rate B/50 |
相对温度指数(RTI) | | | |
冲击w/impact,- |
130 °C | UL 746B | |
电气Elec,- |
130 °C | UL 746B | |
强度w/o impact,- |
130 °C | UL 746B | |
比热容 | 1.25 J/g-°C
| ASTM C 351 | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
68.4 E-6/°C | ASTM E831 | -40°C to 95°C, flow |
导热系数 | 0.25 W/m-°C
| ASTM C 177 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
0.71 mm | UL94 | |
紫外线暴露,水暴露试验和浸渍 | E2 -
| UL 746C | |
辐射板火焰测试 | YES -
| UL Tested | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+17 Ohm-cm
| ASTM D257 | |
介电常数(DK) | | | |
50/60 Hz |
3.17 - | ASTM D150 | |
1MHz |
2.96 - | ASTM D 150 | |
耗散因数(DF) | | | |
50/60 Hz |
9 E-4 | ASTM D 150 | |
1MHz |
100 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | | | |
- |
2 PLC | UL 746A | |
绝缘强度 | 14.9 kV/mm
| ASTM D149 | in air, 3.2 mm |
高电压电弧起痕速率(HVTR) | 2 PLC
| UL 746A | |
热线圈起燃性(HWI) | 2 PLC
| UL 746A | |
高电流弧起燃性(HAI) | 1 PLC
| UL 746A | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 88 %
| ASTM D1003 | 2.54 mm |
雾度 | 1 %
| ASTM D1003 | 2.54 mm |
折射率 | 1.586 -
| ASTM D542 | |