LubriOne™ LB3200-5007 Natural
LubriOne™ LB3200-5007 Natural
PC(聚碳酸酯)
埃万特(原普立万)(Avient)
产品描述
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 耐磨低摩擦 |
| 添加助剂 | 润滑剂 |
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) |
| 颜色形状 | 粒状本色 |
| 成型方式 | 注塑 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.28 g/cm³
| ISO 1183 | |
熔体体积流动速率(MVR) | | | |
300°C/2.16 kg |
4 cm³/10 min | ISO 1133 | |
填充/灰分 | 20 %
| ISO 3451 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
50 Mpa | ISO 527-2 | |
拉伸延伸率 | | | |
断裂(brk) |
15 % | ISO 527-2 | |
拉伸模量 | 2100 Mpa
| ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
10 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
NB kJ/m² | ISO 179 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
141 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
130 °C | ISO 75-2/A | Unannealed |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
0.8 mm | UL94 | |
HB |
1.6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm
| IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm
| IEC 60093 | |
相比漏电起痕指数(CTI ) | | | |
溶液A |
275 V | IEC 60112 | |