LNP™ ELCRIN™ EXL9414B
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
ELCRIN EXL9414B polycarbonate (PC) siloxane copolymer resin is a medium flow, non-chlorinated, non-brominated flame retardant opaque injection molding (IM) grade with major component synthesized from Bio source. This resin offers low temperature ductility (-30°C), thin wall flame retardant capability (UL94 V0 @1.0mm), and in combination with excellent processability and release with opportunities for shorter IM cycle times compared to standard. PC. ELCRIN EXL9414B copolymer resin is a product available in wide range of opaque colors and may be an excellent candidate for a wide variety of applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击阻燃无氯无溴易成型短周期成型易脱模生物基中粘度 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
比重 | 1.19 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
300°C/1.2 kg | 10 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 11.5 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2mm |
横向(Across Flow) | 0.4~0.8 % | Internal | 3.2mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 57 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 60 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5.8 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5.6 % | ISO 527 | 50 mm/min |
断裂(brk) | 107 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 106 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
- | 88 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- | 86 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2190 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2180 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2110 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2140 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 29 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
23℃ (73℉) | 75 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*3 sp=62mm |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 660 J/m | ASTM D256 | |
-30℃ (-22℉) | 46 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 880 J/m | ASTM D256 | |
23℃ (73℉) | 69 kJ/m² | ISO 180/1A | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 67 J | ASTM D3763 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度L | 83 L | ASTM D 785 | |
洛氏硬度R | 117 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 134 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 131 °C | ISO 75/Bf | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 118 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 117 °C | ISO 75/Af | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 136 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 138 °C | ISO 306/B120 | |
相对温度指数(RTI) | |||
冲击w/impact,- | 80 °C | UL 746B | |
电气Elec,- | 80 °C | UL 746B | |
强度w/o impact,- | 80 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 69.1 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 74.2 E-6/°C | ISO 11359-2 | 23°C to 80°C, flow |
横向(Across Flow) | 72.1 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 76.4 E-6/°C | ISO 11359-2 | 23°C to 80°C, xflow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.5 mm | UL94 | Min. |
V-1 | 0.8 mm | UL94 | Min. |
V-0 | 1 mm | UL94 | Min. |
5VB | 1.5 mm | UL94 | Min. |
5VA | 3.1 mm | UL94 | Min. |
氧指数(LOI) | 39 % | ISO 4589 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 960 °C | IEC 60695-2-12 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
表面电阻率 | 1.0E+16 Ohm | ASTM D257 | |
介电常数(DK) | |||
1.1 GHz | 2.78 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 60 E-4 | Internal | |
绝缘强度 | 13 kV/mm | ASTM D149 | in oil, 3.2 mm |