LEXAN™ ML6411
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LEXAN ML6411 polycarbonate (PC) siloxane resin, is a high flow opaque injection molding (IM) grade with very low temperature ductility characteristics. This grade offers UL94 V0 @ 1.5mm and 5VA @ 3.0mm flame retardancy based on non-chlorine, non-bromine FR systems. LEXAN ML6411 resin offers excellent processing characteristics with opportunity for shorter IM cycle times compared to standard PC. This product is available in a wide range of opaque colors and is an excellent candidate for a wide range of electrical applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击阻燃无氯无溴易成型短周期成型高流动 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状不透明色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm³ | ISO 1183 | |
比重 | 1.19 - | ASTM D792 | |
熔体体积流动速率(MVR) | |||
260°C/5.0 kg | 18 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
260°C/2.16 kg | 7 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4~0.8 % | Internal | 3.2 mm |
吸水率 | 0.3 % | ISO 62 | 23°C/sat |
吸湿率 | 0.1 % | ISO 62 | 23°C / 50% RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 62 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 58 Mpa | ISO 527 | 50 mm/min |
断裂(brk) | 54 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 5 % | ASTM D638 | Type I, 50 mm/min |
屈服(yld) | 5 % | ISO 527 | 50 mm/min |
断裂(brk) | 100 % | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 100 % | ISO 527 | 50 mm/min |
弯曲强度 | |||
屈服(yld) | 95 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
屈服(yld) | 90 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 2600 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2350 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 2500 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 2350 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 150 J/m | ASTM D256 | |
-30℃ (-22℉) | 15 kJ/m² | ISO 180/1A | 80*10*3 |
23℃ (73℉) | 900 J/m | ASTM D256 | |
23℃ (73℉) | 60 kJ/m² | ISO 180/1A | 80*10*3 |
仪器化落镖冲击能量 | |||
23℃ (73℉)总能量 | 72 J | ASTM D3763 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 128 °C | ASTM D648 | 6.4 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 125 °C | ISO 75/Be | Edgew 120*10*4 sp=100mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 114 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 119 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 115 °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
维卡软化温度(Vicat) | 134 °C | ASTM D1525 | Rate B/50 |
维卡软化温度(Vicat) | 135 °C | ISO 306 | Rate B/120 |
维卡软化温度(Vicat) | 134 °C | ISO 306 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 100 °C | UL 746B | |
电气Elec,- | 100 °C | UL 746B | |
强度w/o impact,- | 100 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 77 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 70 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 59 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 70 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 0.75 mm | UL94 | Min. |
V-0 | 1.5 mm | UL94 | Min. |
5VB | 1.7 mm | UL94 | Min. |
5VA | 3 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
0.75mm | 960 °C | IEC 60695-2-12 | |
1mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
1.7mm | 960 °C | IEC 60695-2-12 | |
2mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.75mm | 800 °C | IEC 60695-2-13 | |
1.0mm | 800 °C | IEC 60695-2-13 | |
1.5mm | 800 °C | IEC 60695-2-13 | |
1.7mm | 800 °C | IEC 60695-2-13 | |
2.0mm | 800 °C | IEC 60695-2-13 | |
3.0mm | 800 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15 Ohm-cm | IEC 60093 | |
相比漏电起痕指数(CTI ) | |||
- | 250 V | IEC 60112 | |
- | 2 PLC | UL 746A | |
绝缘强度 | 26.5 kV/mm | IEC 60243-1 | in oil, 3.2 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746A | ≥0.75 mm |
热线圈起燃性(HWI) | 2 PLC | UL 746A | ≥3 mm |
高电流弧起燃性(HAI) | 1 PLC | UL 746A | ≥0.75 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746A | ≥1 mm |