LNP™ THERMOCOMP™ DF0041VI
LNP™ THERMOCOMP™ DF0041VI
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP DF0041VI compound is based on Polycarbonate (PC) resin containing 20% glass fiber. Added features of this grade include: Improved Plating Surface and Mechanical Performance suitable for Laser Direct Structuring (LDS) applications, Non-Brominated, Non-Chlorinated Flame Retardant, Wide Processing Window.
基本信息
| 原厂资料 | 物性表(英文) |
| 产品特性 | 阻燃无氯无溴电镀/真空镀激光直接成型(LDS)填充增强 |
| 成型方式 | 注塑 |
| 增强填充 | 20% 玻纤 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.4 g/cm³
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
300℃/1.2 kg |
10 g/10min | ASTM D1238 | |
300℃/2.16 kg |
17 g/10min | ASTM D1238 | |
收缩率 | | | |
纵向(Flow) |
0.2~0.4 % | Internal | |
横向(Across Flow) |
0.2~0.4 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
断裂(brk) |
86 Mpa | ISO 527 | 5 mm/min |
断裂(brk) |
85 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | | | |
断裂(brk) |
2.5 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) |
2.5 % | ISO 527 | 5 mm/min |
弯曲强度 | | | |
- |
125 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
- |
130 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 6000 Mpa
| ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 6400 Mpa
| ISO 178 | 2 mm/min |
拉伸模量 | 7000 Mpa
| ASTM D638 | 5 mm/min |
拉伸模量 | 6900 Mpa
| ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
8 kJ/m² | ISO 179/1eA | V-notch Edgew 80*10*4 sp=62mm |
简支梁无缺口(Charpy Unnotched) | | | |
23℃ (73℉) |
30 kJ/m² | ISO 179/1eU | Edgew 80*10*4 sp=62mm |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
80 J/m | ASTM D256 | |
23℃ (73℉) |
8 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | | | |
23℃ (73℉) |
450 J/m | ASTM D4812 | |
23℃ (73℉) |
30 kJ/m² | ISO 180/1U | 80*10*4 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
124 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
118 °C | ASTM D648 | 3.2 mm, unannealed |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | | | |
1.1 GHz |
3.367 - | Internal | |
1.9 GHz |
3.363 - | Internal | |
5 GHz |
3.347 - | Internal | |
10 GHz |
3.323 - | Internal | |
20 GHz |
3.157 - | Internal | |
耗散因数(DF) | | | |
1.1 GHz |
80 E-4 | Internal | |
1.9 GHz |
50 E-4 | Internal | |
5 GHz |
70 E-4 | Internal | |
10 GHz |
70 E-4 | Internal | |
20 GHz |
70 E-4 | Internal | |