LNP™ THERMOCOMP™ DF002FV
PC(聚碳酸酯)
沙特基础 (SABIC)
产品描述
LNP* Thermocomp* DF002FV compound is a 10% glass fiber reinforced, impact modified PC resin based LDS material solution with stable plating and RF performance. Good surface aesthetics and wide processing window makes it a good candidate for internal and external parts for Laser Direct Structuring applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击良好表面易成型激光直接成型(LDS)填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 增强填充 | 10% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.27 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 29 g/10min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.3 % | Internal | flow, 3.2 mm |
横向(Across Flow) | 0.5 % | Internal | xflow, 3.2 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 60 Mpa | ISO 527 | 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 4.1 % | ASTM D638 | Type I, 5 mm/min |
弯曲强度 | |||
屈服(yld) | 110 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 3600 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
拉伸模量 | 3800 Mpa | ASTM D638 | 5 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 170 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 700 J/m | ASTM D4812 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 125 °C | ASTM D648 | 3.2 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 119 °C | ASTM D648 | 3.2 mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
介电常数(DK) | |||
1.1 GHz | 3.05 - | Internal | |
1.9 GHz | 3.05 - | Internal | |
5 GHz | 3.03 - | Internal | |
耗散因数(DF) | |||
1.1 GHz | 140 E-4 | Internal | |
1.9 GHz | 130 E-4 | Internal | |
5 GHz | 110 E-4 | Internal |