LG PC 8010-10
PC(聚碳酸酯)
乐金LG化学 (LG Chem)
产品描述
Description
It is designed for compounding of PC alloy with high impact strength(low temp.) and excellent ESCR property.
Application
Compound
Key Features
Chemical Resistance, High Impact Resistance, Low Haze, Low Temp. Impact Resistance
基本信息
| 原厂资料 | 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击耐低温冲击ESCR耐化学性 | |||
| 成型方式 | 共混改性 | |||
| 应用产品 | 共混 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.2 g/cm3 | ASTM D792 | |
熔体质量流动速率(MFR) | |||
300℃/1.2 kg | 7 g/10min | ASTM D1238 | |
收缩率 | |||
- | 0.5~0.7 % | ASTM D 955 | |
吸水率 | 0.12 % | ASTM D570 | 24 hrs, 23°C |
吸水率 | 0.2 % | ASTM D570 | equilibrium, 50%RH, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 56 Mpa | ASTM D638 | |
断裂(brk) | 66 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ASTM D638 | |
断裂(brk) | 100 % | ASTM D638 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 640 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | NB J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm2） | 122 °C | ASTM D648 | 4 mm, annealed |
1.8 Mpa (264 psi)（18.6kg/cm2） | 108 °C | ASTM D648 | 4 mm, annealed |
1.8 Mpa (264 psi)（18.6kg/cm2） | 120 °C | ASTM D648 | 4 mm, unannealed |
维卡软化温度(Vicat) | 128 °C | ASTM D1525 | 50°C /hr, 50N Load |
线性膨胀系数(CLTE) | |||
- | 70 E-6/°C | ASTM D 696 | -40 to 82°C |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 0~2 % | ASTM D1003 |
原材料现货供应: