LNP™ LUBRICOMP™ WFL36
PBT
沙特基础 (SABIC)
产品描述
LNP LUBRICOMP* WFL36 is a compound based on PBT resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨填充增强 | |||
| 增强填充 | 30% 玻纤15% PTFE45% 玻纤+PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.68 g/cm³ | ISO 1183 | |
密度 | 1.68 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.1~0.3 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 0.1~0.3 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 0.5~1 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 0.5~1 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.04 % | ISO 62 | 23°C / 50% RH |
吸湿率 | 0.04 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 118 Mpa | ISO 527 | |
断裂(brk) | 117 Mpa | ASTM D638 | |
拉伸延伸率 | |||
断裂(brk) | 2.3 % | ASTM D638 | |
断裂(brk) | 2.2 % | ISO 527 | |
弯曲强度 | |||
- | 193 Mpa | ASTM D790 | |
- | 187 Mpa | ISO 178 | |
弯曲模量 | 10160 Mpa | ASTM D790 | |
弯曲模量 | 10010 Mpa | ISO 178 | |
拉伸模量 | 10340 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 10610 Mpa | ISO 527 | 1 mm/min |
摩擦系数 | 0.57 - | ASTM D 3702 | Dynamic COF |
摩擦系数 | 0.41 - | ASTM D 3702 | Static COF |
磨损因数 | 42 E-10 in5·min/ft·lb·hr | ASTM D 3702 | Wear Factor Washer |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 96 J/m | ASTM D256 | |
23℃ (73℉) | 9 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 683 J/m | ASTM D4812 | |
23℃ (73℉) | 42 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 13 J | ASTM D3763 | |
多轴冲击 | 2 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 217 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 214 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 38.5 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 38.5 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 67.3 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 67.2 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |