LNP™ ELCRIN™ WF0061BiQ
PBT
沙特基础 (SABIC)
产品描述
LNP ELCRIN WF0061BiQ is a 30% glass fiber reinforced, non-brominated, non-chlorinated flame retardant Polybutylene Terephthalate compound, utilizing iQ PBT chemical recycling process of Ocean Bound PET water bottles with minimum 25% post consumer recycled content. Added features of this material include: good flow and UL V-0 rating at 0.8 mm thickness.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定阻燃无氯无溴易成型易脱模耐化学性高流动填充增强含回收料 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.54 g/cm³ | ISO 1183 | |
密度 | 1.57 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
250°C/5.0 kg | 17 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
250°C/5.0 kg | 24 g/10 min | ASTM D1238 | |
收缩率 | |||
纵向(Flow) | 0.4 % | Internal | |
横向(Across Flow) | 0.8 % | Internal | |
吸水率 | 0.08 % | ISO 62-1 | 23°C/24hrs |
吸湿率 | 0.03 % | ISO 62-4 | 23°C/50% RH/24hrs |
回收料含量(PCR) | 28 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 102 Mpa | ISO 527 | 5 mm/min |
断裂(brk) | 104 Mpa | ASTM D638 | Type I, 5 mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ASTM D638 | Type I, 5 mm/min |
断裂(brk) | 2 % | ISO 527 | 5 mm/min |
弯曲强度 | |||
断裂(brk) | 165 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 162 Mpa | ISO 178 | 2 mm/min |
弯曲模量 | 10300 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 10570 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 10800 Mpa | ASTM D638 | 5 mm/min |
拉伸模量 | 10720 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 59 J/m | ASTM D256 | |
-30℃ (-22℉) | 8 kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | 64 J/m | ASTM D256 | |
23℃ (73℉) | 8.5 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 540 J/m | ASTM D4812 | |
23℃ (73℉) | 39 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 5 J | ASTM D3763 | |
23℃ (73℉)总能量 | 6 J | ASTM D3763 | |
多轴冲击 | 1200 N | ASTM D3763 | Peak Force, 23°C |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 217 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 217 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 204 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 202 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
维卡软化温度(Vicat) | 201 °C | ASTM D1525 | Rate B/120 |
维卡软化温度(Vicat) | 200 °C | ASTM D1525 | Rate B/50 |
相对温度指数(RTI) | |||
冲击w/impact,- | 75 °C | UL 746B | |
电气Elec,- | 75 °C | UL 746B | |
强度w/o impact,- | 75 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 22 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
横向(Across Flow) | 85 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
球压痕温度 | 175 °C | IEC 60695-10-2 | approximate maximum |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.8 mm | UL94 | Min. |
5VB | 3 mm | UL94 | Min. |
灼热丝可燃性指数(GWFI) | |||
0.8mm | 960 °C | IEC 60695-2-12 | |
1.5mm | 960 °C | IEC 60695-2-12 | |
3mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.8mm | 750 °C | IEC 60695-2-13 | |
1.5mm | 775 °C | IEC 60695-2-13 | |
3.0mm | 800 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | |
热线圈起燃性(HWI) | 1 PLC | UL 746A | ≥0.8mm |
热线圈起燃性(HWI) | 0 PLC | UL 746A | ≥3mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746A | ≥0.8mm |