LNP™ COLORCOMP™ W1000EXP
PBT
沙特基础 (SABIC)
产品描述
LNP* COLORCOMP* W1000EXP is an unreinforced compound based on PBT resin. Added feature of this grade is a typical viscosity of 5000-7000.
基本信息
| 原厂资料 | 物性表(英文) | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 1.31 - | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 0.9~1.6 % | Internal | flow, 0.75-2.3 mm |
纵向(Flow) | 1.5~2.3 % | Internal | flow, 2.3-4.6 mm |
横向(Across Flow) | 1~1.7 % | Internal | xflow, 0.75-2.3 mm |
横向(Across Flow) | 1.6~2.4 % | Internal | xflow, 2.3-4.6 mm |
吸水率 | 0.08 % | ASTM D570 | 24 hours |
粘度 | 600 Pa-s | Internal | Melt Viscosity |
比容 | 0.76 cm³/g | ASTM D792 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 51 Mpa | ASTM D638 | Type I, 50 mm/min |
断裂(brk) | 51 Mpa | ASTM D638 | Type I, 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 200 % | ASTM D638 | Type I, 50 mm/min |
弯曲强度 | |||
屈服(yld) | 82 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
断裂(brk) | 82 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
弯曲模量 | 2340 Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 53 J/m | ASTM D256 | |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 1602 J/m | ASTM D4812 | |
落锤冲击 | 40 J | ASTM D 3029 | Gardner, 23°C |
落锤冲击 | 40 J | ASTM D 3029 | Modified Gardner, 23°C |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 117 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 154 °C | ASTM D648 | 6.4 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 54 °C | ASTM D648 | 6.4 mm, unannealed |
相对温度指数(RTI) | |||
冲击w/impact,- | 120 °C | UL 746B | |
电气Elec,- | 120 °C | UL 746B | |
强度w/o impact,- | 140 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 81 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 139 E-6/°C | ASTM E831 | 60°C to 138°C, flow |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.83 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 4.0E+16 Ohm-cm | ASTM D257 | |
介电常数(DK) | |||
100Hz | 3.3 - | ASTM D 150 | |
1MHz | 3.1 - | ASTM D 150 | |
耗散因数(DF) | |||
100Hz | 20 E-4 | ASTM D 150 | |
1MHz | 200 E-4 | ASTM D150 | |
相比漏电起痕指数(CTI ) | |||
- | 0 PLC | UL 746A | |
绝缘强度 | 23.2 kV/mm | ASTM D149 | in air, 1.6 mm |
绝缘强度 | 15.7 kV/mm | ASTM D149 | in air, 3.2 mm |
绝缘强度 | 23.2 kV/mm | ASTM D149 | in oil, 1.6 mm |
绝缘强度 | 15.7 kV/mm | ASTM D149 | in oil, 3.2 mm |
耐电弧性 | 4 PLC | UL 746A | Tungsten |
高电压电弧起痕速率(HVTR) | 1 PLC | UL 746A |