Ultradur® B 4330 G6 HR High Speed
PBT
巴斯夫 (BASF)
产品描述
Easy flowing injection-moulding grade containing 30% glass-fibres, for rigid,tough and dimensionally stable technical parts, used in applications with highest demands on hydrolysis resistance such es automotive connectors and housings for electronic units under the hood.
The black colored product Ultradur® B4330 G6 HR High Speed BK15045 has a LS coloration (Laser Sensitive) and can be marked with Nd:YAG lasers.
Abbreviated designation according to ISO 1043: PBT-I-GF30
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性尺寸稳定耐水解填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 应用产品 | 汽车连接器汽车引擎盖下面部件 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.5 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
275°C/2.16 kg | 28 cm³/10 min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | |
横向(Across Flow) | 1 % | ISO 294-4 | |
粘度 | 85 cm³/g | ISO 307, 1157, 1628 | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 130 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
断裂(brk) | 2.6 % | ISO 527-1/-2 | |
弯曲强度 | |||
- | 205 Mpa | ISO 178 | |
弯曲模量 | 8700 Mpa | ISO 178 | |
拉伸模量 | 8880 Mpa | ISO 527-1/-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7.8 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 9 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 52 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 68 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 223 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 205 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 223 °C | ISO 11357-1/-3 | DSC |
加工温度 | 250~280 °C | - | Injection moulding/Extrusion |
模具温度 | 60~100 °C | - | Injection moulding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | IEC 60695-11-10 | |
HB | 1.5 mm | IEC 60695-11-10 |