Ultradur® B 4330 G10 HR
PBT
巴斯夫 (BASF)
产品描述
Impact-modified injection-moulding grade containing 50% glass-fibres, for technical parts,high stiffness,toughness and dimensional stability.Used in applications with highest demands on hydrolysis resistance such as automotive connectors and housings for electronic units under the hood.
The black colored product Ultradur® B4330 G10 HR BK15045 has a LS coloration (Laser Sensitive) and can be marked with Nd:YAG lasers.
Abbreviated designation according to ISO 1043: PBT-I-GF50
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性增韧/冲击改性尺寸稳定耐水解填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 应用产品 | 汽车连接器汽车引擎盖下面部件 | |||
| 增强填充 | 50% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.69 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
275°C/2.16 kg | 10 cm³/10 min | ISO 1133 | |
吸水率 | 0.4 % | ISO 62 | equilibrium in water at 23°C |
吸湿率 | 0.2 % | ISO 62 | equilibrium 23°C/50% r.h. |
粘度 | 108 cm³/g | ISO 307, 1157, 1628 | solution 0,005 g/ml Phenole/1,2 Dichlorbenzol 1:1 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 148 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
断裂(brk) | 2.4 % | ISO 527-1/-2 | |
拉伸模量 | 14500 Mpa | ISO 527-1/-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 12 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 13 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 75 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 80 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 223 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 223 °C | ISO 11357-1/-3 | DSC |
加工温度 | 260~280 °C | - | Injection moulding/Extrusion |
模具温度 | 80~120 °C | - | Injection moulding |